A pic would indicate which batch it is from. If from batch one then it would need to be welded similar to the batch 2 headers to prevent cracking. Batch 1 headers will crack, no if's about it. Sorry, just want to ensure everyone knows what they are getting. They do produce great HP/TQ.
A pic would indicate which batch it is from. If from batch one then it would need to be welded similar to the batch 2 headers to prevent cracking. Batch 1 headers will crack, no if's about it. Sorry, just want to ensure everyone knows what they are getting. They do produce great HP/TQ.
Thank you very much for your much needed input, sir! With that said, please post pics which will definitely help with the sale.
...looks like the 1st batch. There is more welding on the 2nd batch (about 1-1.5" up) between the second and third pipes. To potential buyer, this is still a great buy as this is a great product just make sure that extra welding is added to that area.
...looks like the 1st batch. There is more welding on the 2nd batch (about 1-1.5" up) between the second and third pipes. To potential buyer, this is still a great buy as this is a great product just make sure that extra welding is added to that area.
I believe that was on the Pass. pipe.. Correct me of I'm wrong, but the pass. pipe is the only one that has been cracking?
If I had the funds right now I'd be all over this...just patch the crack spot. If there still available when I get the mulla, I pm'ing you. GL with the sale.